指标 Index |
普通类 The general category |
|
高强类 Gao Qianglei |
||
|
FA |
FC |
FHA |
FHC |
|
Al2O3% ≥ |
70 |
83 |
70 |
80 |
|
常温抗折强渡Mpa 不小于 Room temperature bending force is not less than Mpa |
110℃ |
9 |
9 |
10 |
12 |
|
1100℃ |
5.5 |
6.5 |
10 |
12 |
常温耐压强度Mpa不小于 Room temperature compressive strength is not less than Mpa |
110℃ |
70 |
70 |
70 |
80 |
|
1100℃ |
40 |
50 |
70 |
80 |
1100℃-室温水急冷急热循环5次后抗折强度,Mpa 不小于 The flexural strength at room temperature of 1100 DEG C - water thermal shock after 5 cycles, is not less than Mpa |
4.5 |
5.5 |
5 |
5 |
|
1100℃烧后线变化率,% The rate of change of the temperature of 1100 DEG C line after burning,% |
±0.4 |
±0.5 |
±0.4 |
±0.5 |